The cast and glass reinforced laminates were prepared from Chemifix ISO Catalysed with 1.0% accelerator and 1.5% catalyst. The specimesns were first allowed to cured at room temperature for 24 hours and subsequently post-cured at 80ºC for 6 hours. |
|
|
The cast and glass reinforced laminates were prepared from Chemifix ISO Catalysed with 1.0% accelerator and 1.5% catalyst. The specimesns were first allowed to cured at room temperature for 24 hours and subsequently post-cured at 80ºC for 6 hours. |
|
| Packing : Chemifix ISO is supplied in non-returnable M.S. drums containing 220 kgs. net and HDPE carboys containing 35 kg. net. |
|
Storage & Handling : Chemifix ISO has a flash point 34ºC and classified as flammable. Containers should be kept in a cool, dry and ventilated place away from sunlight and sources of ignition. Under these conditions, the shelf life is 3 months. The storage stability could be further improved by aerating the resin stored in an iterval of about a fortnight. |
|
| "No Smoking" rules should be strictly enforced. In case of fire, suitable extiguishers are dry chemical, form, carbon dioxide or water spray. Containers closed to a fire should be kept cool by spraying with water. |
|
| Spillage may be absorbed onto sand or earth and shovelled off for disposal according to local regulations. |
|
Caution : Store accelerator and catalyst separated. Do not allow them to come in contact with each other as they from violently explosive mixture. It is recommended that the accelerator be blended into the resin first and catalyst be added immediately before use.. |
|
Physioligical & Toxicoligical behavior of Chemifix ISO: The moulding area should be sufficiently ventilated for reducing the styrene vapour levels in the air while moulding. |
|
Skin contact and vapour inhalation must be avoided during moulding becauseof the presence of styrene monomer. In case of irritation in the eye or skin, it is recommended to wash with copious amount of water. In extreme case, seek immediate medical advice. |
| |
|
|